| Grade : | U8 ( Ó8 ) |
| Substitute: | Ó7, Ó10 |
| Classification : | Carbon tool steel |
| Equivalent grades: | Go here |
Chemical composition in % for grade U8 ( Ó8 )
| C | Si | Mn | Ni | S | P | Cr | Cu |
| 0.75 - 0.84 | 0.17 - 0.33 | 0.17 - 0.33 | max 0.25 | max 0.028 | max 0.03 | max 0.2 | max 0.25 |
Temperature of critical points for grade U8 ( Ó8 ).
| Ac1 = 720 , Ar1 = 700 , Mn = 245 |
Mechanical properties under Ò=20oÑ for grade U8 ( Ó8 )
| Assortment | Dimension | Direct. | sâ | sT | d5 | y | KCU | Heat treatment |
| - | mm | - | MPa | MPa | % | % | kJ / m2 | - |
| Blank | 6 | 1420 | 1230 | 10 | 37 | Guenching 780oC, oil, Drawing 400oC, | ||
| Band annealed | 1.5 | 750 | 10 |
| Brinell hardness for U8 ( Ó8 ) (annealing) , GOST 1435-99 | HB 10 -1= 187 MPa |
Technological properties for grade U8 ( Ó8 )
| Weldability: | is not used. |
| Flakes : | not predisposed |
| Temper brittleness: | not predisposed |
Physical properties for grade U8 ( Ó8 )
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
| Grade | MPa | 1/Grade | Watt/(m·Grade) | kg/m3 | J/(kg·Grade) | Ohm·m |
| 20 | 2.09 | 7839 | ||||
| 100 | 2.05 | 11.4 | 49 | 7817 | 477 | 230 |
| 200 | 1.99 | 12.2 | 46 | 7786 | 511 | 305 |
| 300 | 1.92 | 13 | 42 | 7752 | 528 | 395 |
| 400 | 1.85 | 13.7 | 38 | 7714 | 548 | 491 |
| 500 | 1.75 | 14.3 | 35 | 7676 | 565 | 625 |
| 600 | 1.66 | 14.8 | 33 | 7638 | 594 | 769 |
| 700 | 15.2 | 30 | 7600 | 624 | 931 | |
| 800 | 14.5 | 24 | 7852 | 724 | 1129 | |
| 900 | 1165 | |||||
| T | E 10- 5 | a 10 6 | l | r | C | R 10 9 |
Equivalent steels for grade U8 ( Ó8 )
| USA | Germany | Japan | France | England | European | Italy | China | Poland | Czechia | Austria | ||||||||||||||||||||
| - | DIN,WNr | JIS | AFNOR | BS | EN | UNI | GB | PN | CSN | ONORM | ||||||||||||||||||||
|
|
|
|
|
|
|
|
|
|
|
Specification :
| Mechanical properties : | |
| sâ | - Tensile strength , [MPa] |
| sT | - Yield stress, [MPa] |
| d5 | - Specific elongation at fracture , [ % ] |
| y | - Reduction of area , [ % ] |
| KCU | - Impact strength , [ kJ / m2] |
| HB | - Brinell hardness , [MPa] |
Physical properties : | |
| T | - Test temperature , [Grade] |
| E | - Young modulus , [MPa] |
| a | - Coefficient of linear expansion (range 20o - T ) , [1/Grade] |
| l | - Termal (heat) condition coefficient , [Watt/(m·Grade)] |
| r | - Density , [kg/m3] |
| C | - Specific heat ( range 20o - T ), [J/(kg·Grade)] |
| R | - Electrical resistance , [Ohm·m] |
Weldability : | |
| without limitations | - welding is done without heating and subsequent heat treeting |
| limited weldability | - welding is possible under heating up to 100-120 grade and subsequent heat treeting |
| hard weldability | - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing |
Database of steels and alloys (Marochnik) contains information about chemical composition and properties more then 2500 steels and alloys
(stainless steel, alloy steel, carbone steel, structural steel, tool steel,
cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others).
Helpfull for specialists in grade technology, structural engineer, mechanical engineer, metallurgy and metal trader